In situ DRIFTS of NO + O2 reacted with pre-adsorbed NH3 species (A) and NH3 reacted with pre-adsorbed NOx species (B) at 200 °C on the Ho0.45Ce0.35/TiO2 catalyst. from Enhanced low-temperature NH3-SCR performance of Ce/TiO2 modified by Ho catalyst

2019-02-28T16:41:15Z (GMT) by Ting-ting Zhang Li-min Yan
Holmium was used as a dopant to boost the low-temperature NH3-SCR performance of Ce/TiO2 catalyst. It was ascertained that certain amount of Ho-doping species could exceedingly improve the low-temperature SCR activity under 60 000 h−1 of Ce/TiO2, accompanied with the improvement of tolerance to H2O and SO2 at 200°C. Characterization results manifested that Ho modification could not only result in inhibiting the growth of TiO2 crystals and the enlargement of surface specific area but also lead to the enhanced redox ability and the increased amount of surface-adsorbed substances, all of which could promote the low-temperature NH3-SCR performance of Ce/TiO2.