Stress–strain curve statistics for radial tension midsubstance failures from Short cracks in knee meniscus tissue cause strain concentrations, but do not reduce ultimate stress, in single-cycle uniaxial tension
John M. Peloquin
Michael H. Santare
Dawn M. Elliott
10.6084/m9.figshare.7277276.v1
https://rs.figshare.com/articles/dataset/Stress_strain_curve_statistics_for_radial_tension_midsubstance_failures_from_Short_cracks_in_knee_meniscus_tissue_cause_strain_concentrations_but_do_not_reduce_ultimate_stress_in_single-cycle_uniaxial_tension/7277276
Stress–strain curve statistics specifically for radial specimens with midsubstance failures.
2018-10-31 15:55:10
meniscus tear
crack
rupture
mechanical failure
fracture mechanics
tensile test